Sifat Refraktori Batu Bata Korundum
As shown in the Al2O3-Cr2O3 binary phase diagram, Al2O3 and Cr2O3 can form a continuous solid solution without the formation of eutectic. Therefore, adding Cr2O3 to high-purity corundum materials, regardless of the amount added, not only does not reduce the material's refractory properties, but actually improves them. The refractoriness (>1790 ℃) and load softening temperature (>1700 darjah ) bata korundum kromium adalah lebih baik daripada produk-korundum ketulenan tinggi.
Kekuatan Batu Bata Korundum
The room temperature compressive strength of high-purity corundum bricks is generally 70–100 MPa, while the room temperature compressive strength of high-performance chromium corundum bricks is generally >150 MPa, jauh lebih tinggi daripada bata korundum biasa. Ini kerana semasa proses pembakaran, larutan pepejal Al2O3-Cr2O3 terbentuk antara zarah, antara zarah dan serbuk halus, dan antara serbuk halus itu sendiri. Penyelesaian pepejal ini bertindak seperti jambatan, menyambungkan zarah dan serbuk halus, meningkatkan kekuatan bahan dengan ketara.
Kestabilan Kejutan Terma
Menurut laporan, apabila Cr2O3 ditambah kepada korundum, kestabilan kejutan haba berkurangan dengan peningkatan kandungan Cr2O3, terutamanya apabila kandungan Cr2O3 adalah antara 10% dan 66%. Dalam erti kata lain, bata kromium korundum dengan kandungan Cr2O3 yang rendah mempunyai kestabilan kejutan haba yang lebih baik daripada yang mempunyai kandungan Cr2O3 yang tinggi.
Rintangan Hakisan Slag
Keterlarutan pelbagai oksida refraktori dalam sanga arang lebur: Keterlarutan Cr2O3 dalam sanga pengegasan arang batu (SiO2-sistem CaO) dan pelbagai leburan kaca adalah jauh lebih rendah daripada bahan oksida lain. Oleh itu, bahan refraktori yang mengandungi Cr2O3 atau Cr2O3 mempunyai ketahanan yang baik terhadap kakisan daripada sanga keluli, sanga peleburan bukan ferus, sanga pengegasan arang batu, sanga pengegasan minyak dan pelbagai leburan kaca.